Aim of this study is researching the biological and mechanical features of the material, made of ultra-high-molecular-weight-poly-ethylene(UHMWPE) Studing the mechanical features showed that the material prepared with addition of Al2O3 and with using mechanical activation has the highest mechanical features, wear resistance in particular, in comparison with UHMWPE samples without Al2O3 or prepared without mechanical activation. was chosen for. After 60 days orthotopical transplantation this material in rats we did not fined signs of inflammation, cellular infiltration, destruction of material or bone-cartilage defect. Sample was in position of implantation without any shifts. Acquired data shows the perspective-ness of UHMWPE as a material for creating bioimplants for cartilage defects replacement.
Целью данной работы являлось исследование биологических и механических свойств материала, изготовленного из сверхвысокомолекулярного полиэтилена (СВМПЭ). Исследования механических свойств показали, что материал, приготовленный из СВМПЭ с использованием механической активации и с добавкой Al2O3, обладает самыми высокими механическими характеристиками, в частности, наибольшей стойкостью к истиранию по сравнению с образцами СВМПЭ без добавки Al2O3 и не подвергнутого механической активации. Через 60 суток после ортотопической трансплантации образцов из данного материала крысам было отмечено отсутствие каких-либо признаков воспаления, клеточной инфильтрации, разрушения образца и дальнейшего разрушения костно-хрящевого дефекта. Образец оставался на месте имплантации без смещений. Полученные данные свидетельствуют о перспективности использования СВМПЭ в качестве материала для создания имплантатов для замещения хрящевых дефектов.